Synthesis of New Complex Ferrite Li0.5MnFe1.5O4, Chemical – Physical and Electrophysical Research
Дата публикации
12 июня 2024 г.
Тип
preprint
Журнал
Preprints.org
Аннотация
In this article, the sol-gel method was used as a synthesis method, which shows the physico –chemical nature of the synthesis of a new complex material ferrit Li0.5MnFe1.5O4. The synthesized structure and structure were determined by the method of X-ray phase analysis. According to the analysis indicators, it was found that our compound is single-phase, spinel-structured, and syngony - cubic type. The microstructure of the compound and the quantitative composition of the elements contained were analyzed under a scanning electron microscope (SEM). Through a scanning electron microscope, Microsystems were taken from different parts of l Li0.5MnFe1.5O4-type crystallite, the elemental composition of crystals was analyzed, and the general type of surface layer of complex ferrite was shown. As a result, the fact that the compound consists of a single phase, the clarity of its construction was determined by the topography and chemical composition of the compound. As a result, it was found that the newly synthesized complex ferrites correspond to the Formula Li0.5MnFe1.5O4. The particles of the formed compounds have a large size (between 50.0 μm, 20.0 μm and 10.0 μm). Electro physical measurements were carried out on the LCR - 800 unit at intervals of 293-483 K and at frequencies of 1.5 and 10 kHz. The increase in frequency to 10 kHz led to a decrease in the value ε in the range of the studied temperature (293-483 K).
Области науки (FoS)